Patent attributes
A titanium-containing calcium hexaaluminate material and preparation method thereof is disclosed. The technical solution is: using 60˜80 wt % alumina micro powder, 5˜20 wt % calcium-containing micro powder, 10˜20 wt % titania micro powder and 1˜10 wt % manganese oxide micro powder as raw materials, blending the raw materials evenly in a planetary ball mill to obtain a blend, machine pressing the blend at 100˜200 MPa to obtain a green body, drying the green body at 110˜200° C. for 12˜36 h, and incubating the dried green body at 1500˜1800° C. for 1˜8 h to obtain the titanium-containing calcium hexaaluminate material. The present disclosure has low cost and simple process, and the prepared titanium-containing calcium hexaaluminate material has the characteristics of good chemical stability, high thermal shock resistance and strong melt resistance to titanium-aluminum alloy.